FinFETs with strained well regions

ABSTRACT

A device includes a substrate and insulation regions over a portion of the substrate. A first semiconductor region is between the insulation regions and having a first conduction band. A second semiconductor region is over and adjoining the first semiconductor region, wherein the second semiconductor region includes an upper portion higher than top surfaces of the insulation regions to form a semiconductor fin. The semiconductor fin has a tensile strain and has a second conduction band lower than the first conduction band. A third semiconductor region is over and adjoining a top surface and sidewalls of the semiconductor fin, wherein the third semiconductor region has a third conduction band higher than the second conduction band.

PRIORITY CLAIM AND CROSS-REFERENCE

This application is a continuation of U.S. patent application Ser. No. 15/253,958, entitled “FinFETs with Strained Well Regions,” filed on Sep. 1, 2016, which is a continuation of U.S. patent application Ser. No. 14/725,299, entitled “FinFETs with Strained Well Regions,” filed on May 29, 2015, now U.S. Pat. No. 9,455,320 issued Sep. 27, 2016, which application is a divisional of U.S. patent application Ser. No. 13/779,015, entitled “FinFETs with Strained Well Regions,” filed on Feb. 27, 2013, now U.S. Pat. No. 9,087,902 issued Jul. 21, 2015, which applications are incorporated herein by reference.

BACKGROUND

The speed of metal-oxide-semiconductor (MOS) transistors are closely related to the drive currents of the MOS transistors, which are further closely related to the mobility of charges in the channels of the MOS transistors. For example, NMOS transistors have high drive currents when the electron mobility in their channel regions is high, while PMOS transistors have high drive currents when the hole mobility in their channel regions is high. Germanium, silicon germanium, and compound semiconductor materials (referred to as III-V compound semiconductors hereinafter) comprising group III and group V elements are thus good candidates for forming their high electron mobility and/or hole mobility.

Germanium, silicon germanium, and III-V compound semiconductor regions are also promising materials for forming the channel regions of Fin Field-Effect transistors (FinFETs). Methods and structures for further improving the drive currents on the FinFETs are currently being studied.

BRIEF DESCRIPTION OF THE DRAWINGS

For a more complete understanding of the embodiments, and the advantages thereof, reference is now made to the following descriptions taken in conjunction with the accompanying drawings, in which:

FIGS. 1 through 9C are cross-sectional views of intermediate stages in the manufacturing of a semiconductor fin and a Fin Field-Effect Transistor (FinFET) in accordance with some exemplary embodiments; and

FIG. 10 illustrates a band diagram of a plurality of semiconductor regions in the FinFET.

DETAILED DESCRIPTION

The making and using of the embodiments of the disclosure are discussed in detail below. It should be appreciated, however, that the embodiments provide many applicable concepts that can be embodied in a wide variety of specific contexts. The specific embodiments discussed are illustrative, and do not limit the scope of the disclosure.

Fin Field-Effect Transistors (FinFETs) and methods of forming the same are provided in accordance with various exemplary embodiments. The intermediate stages of forming the FinFETs in accordance with some embodiments are illustrated. The variations of the embodiments are discussed. Throughout the various views and illustrative embodiments, like reference numbers are used to designate like elements.

Referring to FIG. 1, substrate 20 is provided. Substrate 20 may be a semiconductor substrate such as a crystalline silicon substrate. Substrate 20 may also include silicon, germanium, carbon, or the like. Insulation regions such as Shallow Trench Isolation (STI) regions 22 are formed in substrate 20. STI regions 22 may be formed by recessing semiconductor substrate 20 to form trenches, and then filling the trenches with dielectric materials such as silicon oxide. A Chemical Mechanical Polish (CMP) is then performed to remove excess portions of the dielectric materials, and the remaining portions are STI regions 22. The top surfaces of STI regions 22 are thus level with the top surface of substrate 20.

STI regions 22 include neighboring regions having their sidewalls facing each other. Portions 20′ of substrate 20 extend between the neighboring STI regions. Width W1 of substrate portions 20′ may be between about 10 nm and about 200 nm. It is appreciated that the dimensions recited throughout the description are merely examples, and may be changed to different values. The neighboring STI regions may be separate regions, or may be portions of a continuous region, which may form a STI ring in some embodiments.

Referring to FIG. 2, substrate portions 20′ are recessed, forming recesses 24 between neighboring STI regions 22. In some embodiments, the bottoms of recesses 24 are higher than the bottom surfaces of STI regions 22. In alternative embodiments, the bottoms of recesses 24 are substantially level with or lower than the bottoms of STI regions 22.

Referring to FIG. 3, semiconductor regions 26 are grown in recesses 24 through epitaxy. The top surfaces of semiconductor regions are lower than the top surfaces of STI regions 22. Semiconductor regions 26 may have a first lattice constant greater than the lattice constant of substrate 20. In some embodiments, semiconductor regions 26 comprises silicon germanium, which is expressed as Sil-xGex, wherein value X is the atomic percentage of germanium in semiconductor regions 26, which atomic percentage may be between about 0.2 (20 percent) and 1 (100 percent) in exemplary embodiments. Semiconductor regions 26 are a relaxed semiconductor region, which means that at least the top portions of semiconductor regions are relaxed with substantially no stress. This may be achieved by, for example, making thickness T1 great enough, since the stresses in upper portions of semiconductor regions 26 are increasingly smaller than the lower portions. In some exemplary embodiments, thickness T1 is greater than about 30 nm, and may be between about 30 nm and about 150 nm. In some exemplary embodiments, the conduction band of semiconductor regions 26 is lower than the conduction band of bulk silicon by between about 0.036 eV and about 0.144 eV, wherein the conduction band of silicon is about 1.1 eV. FIG. 10 schematically illustrates bandgap BG1, conduction band Ec1, and valence band Ev1 of semiconductor regions 26.

Next, referring to FIG. 4, semiconductor regions 28 are grown in recesses 24 through epitaxy, wherein semiconductor regions 28 are grown over and contacting semiconductor regions 26. Semiconductor regions 28 have a tensile strain, and may be un-doped with n-type and p-type impurities. In some embodiments, the tensile strain is generated by making the lattice constant of semiconductor regions 28 smaller than the lattice constant of semiconductor regions 26. In some embodiments, the tensile strain is higher than about 1.36 MPa, and may be higher than about 6.8 GPa. Semiconductor regions 28 include portions in recesses 24 (FIG. 3), which portions have thickness T2. Thickness T2 is small enough, so that after the subsequent Chemical Mechanical Polish (CMP) in FIG. 5, semiconductor regions 28 are not relaxed and have the tensile strain. In some exemplary embodiments, thickness T2 is smaller than about 150 nm, and may be between about 30 nm and about 150 nm.

FIG. 10 schematically illustrates bandgap BG2, conduction band Ec2, and valence band Ev2 of semiconductor regions 28. Conduction band Ec2 is lower than the conduction band Ec1 of semiconductor regions 26, with the difference (Ec1−Ec2) being greater than about 0.036 eV, for example. In some embodiments, semiconductor regions 28 comprise Sil-yGey, wherein value Y is the atomic percentage of germanium in semiconductor regions 28. Value Y may be smaller than about 0.3 (30 percent), and may be between 0 and about 0.3. Value Y may also be equal to 0, which means that semiconductor regions 28 are silicon regions free from germanium. Furthermore, value Y is smaller than value X of semiconductor regions 26, with the difference (X−Y) being greater than about 0.1, greater than about 0.3, or greater than about 0.5, for example. A greater difference (X−Y) may advantageously result in a greater tensile strain in semiconductor regions 28, and a greater conduction band difference (Ec1−Ec2).

Semiconductor regions 28 may be grown to a level higher than the top surfaces of STI regions 22. A CMP is then performed to level the top surface of STI regions 22 and semiconductor regions 28. The resulting structure is shown in FIG. 5. In alternative embodiments, the growth of semiconductor regions 28 stops at a time when the top surface of semiconductor regions 28 is level with or lower than the top surfaces of STI regions 22. In these embodiments, the CMP may be performed, or may be skipped.

Referring to FIG. 6, STI regions 22 are recessed, for example, through an etching step. The top surfaces 22A of the remaining STI regions 22 are higher than the interfaces 27 between semiconductor regions 26 and semiconductor regions 28. The portions of semiconductor regions 28 that are higher than top surfaces 22A are referred to as semiconductor fins 30 hereinafter.

FIG. 7 illustrates the formation of semiconductor regions 34, which are epitaxially grown on the exposed top surfaces and sidewalls of semiconductor fins 30. Semiconductor regions 34 are substantially conformal layers, with the portions on the top surfaces of semiconductor fins 30 having substantially the same thickness T3 as the portions on the sidewalls of semiconductor fins 30. In some embodiments, thickness T3 is between about 5 nm and about 150 nm.

Bandgap BG3, conduction band Ec3, and valence band Ev3 of semiconductor regions 34 are schematically illustrated in FIG. 10. Conduction band Ec3 is higher than conduction band Ec2 of semiconductor regions 28, with the difference (Ec3−Ec2) being greater than about 0.036 eV, for example. In some embodiments, semiconductor regions 34 comprise Sil-zGez, wherein value Z is the atomic percentage of silicon in semiconductor regions 34. Value Z may be greater than about 0.3, and maybe between about 0.3 and 1. Value Z may also be equal to 1, which means that semiconductor regions 34 are pure germanium regions free from silicon. Furthermore, value Z is greater than value Y of semiconductor regions 28, with the difference (Z−Y) being greater than about 0.1, or greater than about 0.3, for example. A greater difference (Z−Y) may advantageously result in a greater conduction band difference (Ec3−Ec2).

In some embodiments, semiconductor regions 34 include layers 34A and layers 34B, which are formed over layers 34A. Layers 34A and layers 34B may have substantially the same atomic percentage of silicon and substantially the same atomic percentage of germanium, although their compositions may also be different from each other. In some exemplary embodiments, layers 34A are not doped with n-type impurities, and may also be free from p-type impurities. In alternative embodiments, layers 34A are n-type doped layers with the n-type impurity concentration lower than about 1016/cm 3, for example. Thickness T4 of layers 34A may be greater than 0 nm and smaller than about 50 nm. Layers 34B are n-type layers, wherein the n-type impurity concentration in layers 34B may be higher than about 1018/cm 3. In these embodiments, the n-type impurity concentration in layers 34A is lower than the n-type impurity concentration in layers 34B. Layers 34B act as the electron-supply layers for supplying electrons to the underlying carrier channels 46 (FIGS. 9A through 9C).

The doped n-type impurity may include phosphorous, arsenic, antimony, or combinations thereof. Layers 34A and layers 34B may be formed in-situ in a same vacuum chamber, and may be formed using essentially the same process conditions, except that in the formation of layers 34A, no n-type dopant is added, while the n-type dopant is added in the formation of layers 34B. Alternatively, in the formation of both layers 34A and 34B, n-type dopants are added, and the n-type dopant amount for forming layers 34A is smaller than that for forming layers 34B. In some embodiments, thickness T5 of doped layers 34B is between about 1 nm and about 20 nm.

In some embodiments, semiconductor regions 34 further include layers 34C over layers 34B. Layers 34C may have atomic percentages of silicon and germanium same as either one, or both, of layers 34A and 34B. In alternative embodiments, the silicon and germanium atomic percentages in layers 34A, 34B, and 34C are all different from each other. Layers 34C may also be un-doped with n-type impurities, or doped with n-type impurities that have a lower impurity concentration than the respective underlying layers 34B. In alternative embodiments, layers 34C are not formed, and the respective structure may be found in FIG. 9B.

FIG. 8 illustrates the formation of silicon caps 36, which may be substantially pure silicon regions with no germanium added. Silicon caps 36 may also be formed through epitaxy, and hence are over the top portions and sidewall portions of semiconductor regions 34. In some embodiments, no n-type and p-type impurities are added into silicon caps 36, although n-type and p-type impurities with low concentrations, for example, lower than about 1016/cm 3, may also be added. Thickness T6 of silicon caps 36 may be between about 1 nm and about 20 nm in some embodiments. In alternative embodiments, silicon caps 36 are not formed.

The structure shown in FIG. 8 may be used to form FinFET 38, as shown in FIGS. 9A, 9B, and 9C. Referring to FIG. 9A, gate dielectric 40 and gate electrode 42 are formed. Gate dielectric 40 may be formed of a dielectric material such as silicon oxide, silicon nitride, an oxynitride, multi-layers thereof, and/or combinations thereof. Gate dielectric 40 may also be formed of high-k dielectric materials. The exemplary high-k materials may have k values greater than about 4.0, or greater than about 7.0. Gate electrode 42 may be formed of doped polysilicon, metals, metal nitrides, metal silicides, and the like. The bottom ends of gate dielectric 42 may contact the top surfaces of STI regions 22. After the formation of gate dielectric 40 and gate electrode 42, source and drain regions 50 (FIG. 9C) are formed.

As shown in FIG. 9A, semiconductor regions 28 form interfaces 44 with the adjoin semiconductor regions 34. Carrier channels 46, which are alternatively referred to as Two-Dimensional Electron Gas (2DEG) channels, are formed and located in semiconductor regions 28. 2DEG channels 46 may also be close to interfaces 44. Although semiconductor regions 28 may not be doped with n-type impurities, carrier channels 46 still have a high density of electrons, which are supplied by the respective overlying electron-supply layers 34B.

FIG. 9B illustrates a cross-sectional view of FinFET 38 in accordance with alternative embodiments. These embodiments are essentially the same as the embodiments in FIG. 9A, except that no layer 34C is formed. Accordingly, silicon caps 36 are in physical contact with the respective underlying layers 34B.

FIG. 9C illustrates a cross-sectional view of FinFET 38, wherein the cross-sectional view is obtained from the plane crossing line 9C-9C in FIG. 9A. Source and drain regions 50 are formed on the opposite sides of gate dielectric 40 and gate electrode 42. Source and drain regions 50 are doped with an n-type impurity such as phosphorous, arsenic, antimony, or the like, and hence the respective FinFET 38 is an n-type FinFET. 2DEG channel 46 interconnects the source and drain regions 50.

FIG. 10 schematically illustrates a band diagram of semiconductor regions 26, 28, and 34. As shown in FIG. 10, the conduction band Ec2 of semiconductor region 28 is lower than conduction band Ec1 of semiconductor region 26 and conduction band Ec3 of semiconductor region 34. Accordingly, conduction bands Ec1, Ec2, and Ec3 form a well, with conduction band Ec2 forming the bottom of the well. Electrons 48, which are supplied by electron-supply layers 34B (FIGS. 9A and 9B), are confined in the well to form the 2DEG channels. The formation of the well is attributed to that semiconductor region 28 is tensile strained, and hence conduction band Ec2 is suppressed to a level lower than conduction bands Ec1 and Ec3. As a comparison, if semiconductor region 28 is not tensile strained, the conduction band of semiconductor region 28 will be higher than the conduction bands of semiconductor regions 26 and 34, and hence the well region and the 2DEG channel will not be formed. In addition, since semiconductor region 28 may not be doped with impurities, electrons can move freely without collision or with substantially reduced collisions with the impurities.

In the embodiments of the present disclosure, by forming relaxed semiconductor region 26 that has a greater lattice constant than the lattice constant of semiconductor region 28, the overlying semiconductor region 28 may have a tensile strain. The tensile strain results in a conduction band well to be formed in semiconductor region 28. Furthermore, electron-supply layer 34B is formed overlying semiconductor region 28 to supply electrons, which are confined in the well formed in semiconductor region 28 to form the 2DEG channel. Accordingly, the resulting FinFET has a high saturation current.

In accordance with some embodiments, a device includes a substrate and insulation regions over a portion of the substrate. A first semiconductor region is between the insulation regions and having a first conduction band. A second semiconductor region is over and adjoining the first semiconductor region, wherein the second semiconductor region includes an upper portion higher than top surfaces of the insulation regions to form a semiconductor fin. The semiconductor fin has a tensile strain and has a second conduction band lower than the first conduction band. A third semiconductor region is over and adjoining a top surface and sidewalls of the semiconductor fin, wherein the third semiconductor region has a third conduction band higher than the second conduction band.

In accordance with other embodiments, a device includes a silicon substrate and STI regions over a portion of the silicon substrate. A first SiGe region is located between and in contact with the STI regions, wherein the first SiGe region has a first germanium atomic percentage. A silicon-containing region is over the first SiGe region, with edges of the silicon-containing region vertically aligned to respective edges of the first SiGe region. The silicon-containing region has a tensile stress. A second SiGe region contacts a top surface and sidewalls of the silicon-containing region. The second SiGe region has second germanium atomic percentage. The first and the second germanium atomic percentages are higher than a third germanium atomic percentage of the silicon-containing region. The device further includes a gate dielectric over the second SiGe region, a gate electrode over the gate dielectric, and a source region and a drain region on opposite sides of the gate dielectric and the gate electrode.

In accordance with yet other embodiments, a method includes recessing a portion of a substrate between two insulation regions to form a recess, performing a first epitaxy to grow a first semiconductor region in the recess, and performing a second epitaxy to grow a second semiconductor region in the recess. The first semiconductor region is relaxed. The second semiconductor region is over and contacting the first semiconductor region. The second semiconductor region has a tensile strain. A planarization is performed to level top surfaces of the second semiconductor region and the insulation regions. The insulation regions are recessed, wherein a top portion of the second semiconductor region over the insulation regions forms a semiconductor fin. A third epitaxy is performed to grow a third semiconductor region on a top surface and sidewalls of the semiconductor fin. The second semiconductor region has a conduction band lower than conduction bands of the first and the third semiconductor regions.

Although the embodiments and their advantages have been described in detail, it should be understood that various changes, substitutions and alterations can be made herein without departing from the spirit and scope of the embodiments as defined by the appended claims. Moreover, the scope of the present application is not intended to be limited to the particular embodiments of the process, machine, manufacture, and composition of matter, means, methods and steps described in the specification. As one of ordinary skill in the art will readily appreciate from the disclosure, processes, machines, manufacture, compositions of matter, means, methods, or steps, presently existing or later to be developed, that perform substantially the same function or achieve substantially the same result as the corresponding embodiments described herein may be utilized according to the disclosure. Accordingly, the appended claims are intended to include within their scope such processes, machines, manufacture, compositions of matter, means, methods, or steps. In addition, each claim constitutes a separate embodiment, and the combination of various claims and embodiments are within the scope of the disclosure. 

What is claimed is:
 1. A device comprising: a substrate; insulation regions over a portion of the substrate; a first semiconductor region between the insulation regions; a second semiconductor region over and adjoining the first semiconductor region, wherein the second semiconductor region comprises an upper portion higher than top surfaces of the insulation regions to form a semiconductor fin; a third semiconductor region over the semiconductor fin, wherein the third semiconductor region comprises at least a first sub layer doped with an n-type impurity, wherein the first, the second and the third semiconductor regions are formed of different materials; a silicon cap over the third semiconductor region, wherein the silicon cap is free from n-type and p-type impurities; and a source region and a drain region on opposite sides of the semiconductor fin.
 2. The device of claim 1, wherein the second semiconductor region is intrinsic.
 3. The device of claim 1, wherein the third semiconductor region extends from the source region to the drain region.
 4. The device of claim 1, wherein the first semiconductor region and the third semiconductor region comprise silicon germanium, and have germanium atomic percentages higher than an atomic percentage of the second semiconductor region.
 5. The device of claim 1, wherein the third semiconductor region comprises: a second sub layer on sidewalls and a top surface of the semiconductor fin, wherein the first sub layer is over the second sub layer, and the second sub layer is an un-doped layer substantially free from n-type impurities.
 6. The device of claim 5, wherein the third semiconductor region further comprises a third sub layer overlying the first sub layer, and the third sub layer is substantially free from n-type impurities.
 7. The device of claim 6, wherein each of the first sub layer, the second sub layer, and the third sub layer comprises silicon germanium, and atomic percentages of silicon in the first sub layer, the second sub layer, and the third sub layer are equal to each other, and atomic percentages of germanium in the first sub layer, the second sub layer, and the third sub layer are equal to each.
 8. The device of claim 1, wherein the second semiconductor region has a conduction band lower than conduction bands of the first semiconductor region and the third semiconductor region.
 9. A device comprising: a silicon substrate; Shallow Trench Isolation (STI) regions extending into the silicon substrate; a semiconductor fin protruding higher than top surfaces of the STI regions, wherein the semiconductor fin is between opposite portions of the STI regions; a silicon germanium region contacting a top surface and sidewalls of the semiconductor fin, wherein the silicon germanium region comprises: a first sub layer having a first n-type impurity concentration; and a second sub layer over the first sub layer, wherein the second sub layer has a second n-type impurity concentration higher than the first n-type impurity concentration; a gate dielectric over the silicon germanium region; a gate electrode over the gate dielectric; and a source region and a drain region on opposite sides of the gate dielectric and the gate electrode, wherein the source region and the drain region are n-type regions, and wherein the silicon germanium region extends from the source region and the drain region.
 10. The device of claim 9, wherein the first sub layer is free from p-type impurities.
 11. The device of claim 10 further comprising a third sub layer over the second sub layer, and the third sub layer is free from both n-type impurities and n-type impurities.
 12. The device of claim 9, wherein the semiconductor fin is intrinsic.
 13. The device of claim 9 further comprising an additional silicon germanium region located between and in contact with the STI regions, wherein the additional silicon germanium region is relaxed.
 14. The device of claim 9 further comprising a silicon cap over the silicon germanium region, wherein the silicon cap is substantially free from germanium, and the silicon cap is intrinsic.
 15. A device comprising: a silicon germanium region comprising: a first layer having a first n-type impurity concentration; a second layer over the first layer, wherein the second layer has a second n-type impurity concentration; and a third layer over the second layer, wherein the third layer has a third n-type impurity concentration, and the second n-type impurity concentration is higher than both the first n-type impurity concentration and the third n-type impurity concentration; a gate dielectric over the silicon germanium region; a gate electrode over the gate dielectric; and a source region and a drain region on opposite sides of the gate dielectric and the gate electrode.
 16. The device of claim 15, wherein the first layer and the third layer are substantially free from n-type impurities.
 17. The device of claim 16, wherein the first layer and the third layer are further free from p-type impurities.
 18. The device of claim 15 further comprising a silicon layer free from germanium between the third layer and the gate dielectric, wherein the silicon layer and the silicon germanium region extend from the source region to the drain region, and the silicon layer is undoped with p-type and n-type impurities.
 19. The device of claim 15 further comprising: isolation regions; and a semiconductor fin protruding higher than top surfaces of the isolation regions, wherein the silicon germanium region is on a top surface and sidewalls of the semiconductor fin, and the semiconductor fin is undoped with p-type and n-type impurities.
 20. The device of claim 15, wherein the first layer, the second layer, and the third layer have a same germanium atomic percentage. 